ENGAGE™ HM 7487
| Category: | TPO (POE) , Polyolefin Elastomer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ENGAGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 60RgQV_ENGAGE-HM-7487.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ENGAGE™ HM 7487 Polyolefin Elastomer is an ethylene-butene copolymer with higher molecular weight, better toughness, and higher melt strength than other commercially available polyolefin elastomers. It can serve as an extender for SEBS, impart lower gloss in hard TPOs, provide the basis for flexible soft-touch compounds, and is well suited for extruded applications such as wire and cable. ENGAGE HM 7487 is also useful for impact modification of various thermoplastic resins. Main Characteristics:
Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.860 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | < 0.50 | g/10 min | ASTM D1238 |
| Mooney Viscosity (ML 1+4, 121°C) | 47 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 1 sec, Compression Molded | 58 | ||
| Shore D, 1 sec, Compression Molded | 14 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Break, Compression Molded | 2.40 | MPa | |
| 100% Strain, Compression Molded | 1.50 | MPa | |
| Tensile Elongation 2(Break, Compression Molded) | > 600 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : Compression Molded | 1.90 | MPa | |
| 2% Secant : Compression Molded | 1.20 | MPa |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 3 | 28.0 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -57.0 | °C | Internal Method |
| Melting Temperature (DSC) 4 | 37.0 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 17.0 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | Die C |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Conpol™ 13B | DuPont Packaging & Industrial Polymers | EMAA | Conpol™ |
| HiPrene® MT43 | GS Caltex | PP, Unspecified | HiPrene® |
| ICORENE® 3935 | ICO Polymers SA, A Division of A. Schulman | PE Copolymer | ICORENE® |
| LEXAN™ LUX2910T_ resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Sylvin 9980-95 White 1461 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |