KARINTOX 70/6
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | KARINTOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 60Dlmk_KARINTOX-70-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KARINTOX WAS SPECIALLY DEVELOPED. IT IS A THERMOPLASTIC POLYOLEFIN, FLAME RETARDANT, NON-HALOGEN AND LOW SMOKE EMISSION RECOMMENDED FOR ELECTRICAL COATING FOR CABLES UNTIL 1KV. FOR A BETTER USAGE/PROCESSING WE SUGGEST A PRE-WARM/HEAT ( 2 HOURS IN 70-80C ) MAINLY AFTER BEING STOCKED FOR A LONG TIME. LOW COMPRESSION SCREWS ( 1.2:1 IS THE IDEAL ) AND CLEAVING - THERMICAL PROFILE FROM 140C TO 165C AND MELTING TEMPERATURES NO MORE THAN 180C. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.39 to 1.45 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -1.28 to 1.72 | ME 12 | |
| Color b | 1.77 to 4.77 | ME 12 | |
| Color L | 87.6 to 90.6 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Moisture | < 600 | ppm | ME 52 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cold Bend (-15°C) | OK | IEC 60811-1-4 | |
| Hot Deformation (80°C) | 30.0 | NBR 6239 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Smoke Density - Transmittance | 75 | % | NBR 11300 |
| Toxicity | 0.650 | NBR 12139 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Corrosivity of Gases | 5.00 µS/mm 5.60 pH | NBR 11633 | |
| Halogen Acid Gas Evolution | 0.00 | mg/g | NBR 10495 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 20 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 20 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 50 to 54 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 12.6 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 150 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 10.0 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 130 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -35.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 36 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F200 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| tefanyl® VR VRGR 820 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| TEREZ PA/ABS Blend 2010/2 UV | TER HELL PLASTIC GMBH | Nylon 6+ABS | TEREZ PA/ABS |
| Hylex® P1010G20 | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| CYCOLAC™ MG47 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |