Pro-fax RP913J
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 60BdZ1_Pro-fax-RP913J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax RP913J clarified random copolymer polypropylene is available in pellet form. This resin is typically used in sheet extrusion/thermoforming and other rigid packaging applications. For regulatory compliance information see Pro-fax RP913J Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 37.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 10 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1590 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 109 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1140 µm) | 23 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiprene® 4045 | Resirene, S.A. de C.V. | TPE | Resiprene® |
| Wanthane® WHT-1490IV | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Novalloy-B B5723 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |
| APEX® 1523F3 | Teknor Apex Company | PVC, Flexible | APEX® |
| LUVOCOM® 1-8981/LCF | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |