LNP™ STAT-KON™ DX09301C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5xkcEO_LNP-STAT-KON-DX09301C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low Ionic, Low Outgassing, Low LPC and ESD safe Polycarbonate compound suitable for Semiconductor and Hard Disk Drive (HDD) application. Added features of this material include: Clean Compounding System. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.22 | g/cm³ | ASTM D792 |
| -- | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.50 to 0.70 | % | |
| Across Flow : 24 hr | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2680 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.9 | MPa | ASTM D638 |
| Yield | 66.0 | MPa | ISO 527-2/5 |
| Break 3 | 51.7 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.4 | % | ASTM D638 |
| Yield | 3.1 | % | ISO 527-2/5 |
| Break 5 | 15 | % | ASTM D638 |
| Break | 12 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2600 | MPa | ASTM D790 |
| -- 7 | 2560 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 99.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 9 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2200 | J/m | ASTM D4812 |
| 23°C 10 | 200 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 8.18 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 138 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 137 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+7 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+7 | ohms·cm | ASTM D257 |
| Static Decay 12 | 0.1 | sec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 295 to 305 | °C | |
| Middle Temperature | 310 to 320 | °C | |
| Front Temperature | 320 to 330 | °C | |
| Processing (Melt) Temp | 305 to 325 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.200 to 0.300 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PBT TE5001D | Sincerity Australia Pty Ltd. | PC+PBT | Sindustris PBT |
| Sylvin 9077-95 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| NEMCON H PA DP117/X3 | Ovation Polymers Inc. | PEEK | NEMCON H |
| Hostacom PPN 1034 12 | LyondellBasell Industries | PP Copolymer | Hostacom |
| POLYCASA® PC UVP | Polycasa | PC | POLYCASA® |