TAROLOX 10 Z1 G6
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5xKN9b_TAROLOX-10-Z1-G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT glass fibre reinforced 30%, improved impact resistance, good flow, good surface finish, good mechanical and thermal properties, good dimensional stability. Available: differents colours, heat stabilised (H), heat and hydolysis improved (H2). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 to 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 to 0.40 | % | |
| Across Flow | 0.40 to 0.80 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.040 | % | ASTM D570, ISO 62 |
| Saturation | 0.20 | % | ASTM D570 |
| Saturation, 23°C | 0.20 | % | ISO 62 |
| Granule Humidity | < 0.050 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 160 | MPa | ISO 178 |
| Break | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 14 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 205 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 2 | 100 | °C | |
| -- 3 | 130 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50, ASTM D1525 4 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 225 | °C | ASTM D211, ISO 121 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.970 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 20000 hrs |
| 3 . | Heat Stabilized, 20000 hrs |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALCOM® PC 740/4 GY1122-04LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| apinat® DP2267 | API SpA | Biodeg Polymers | apinat® |
| Exxtral™ Performance Polyolefin HMU404 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Ferro PP LPP35BF54HB-WH | Ferro Corporation | PP, Unspecified | Ferro PP |
| Gallonprene® GP420-7007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |