Desmopan® DP 3065D
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5wdeQi_Desmopan-DP-3065D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; high mechanical strength; excellent abrasion resistance; good wear resistance; very short cycle times; Application; Technical parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1220 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 98 | ||
| Shore D, 15 sec | 65 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break, 23°C | 69.0 | MPa | |
| 10% Strain, 23°C | 21.9 | MPa | |
| 50% Strain, 23°C | 29.4 | MPa | |
| 100% Strain, 23°C | 32.5 | MPa | |
| 300% Strain, 23°C | 55.7 | MPa | |
| Tensile Strain 4(Break, 23°C) | 350 | % | DIN 53504 |
| Flexural Modulus 5(23°C) | 350 | MPa | ISO 178 |
| Abrasion Resistance (23°C) | 18.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 2.62 | GPa | |
| 20°C | 0.948 | GPa | |
| 60°C | 0.264 | GPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience (23°C) | 50 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 6(23°C) | 180 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 26 | % | |
| 70°C, 24 hr | 38 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 110 | °C | |
| Processing (Melt) Temp | 225 to 245 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Automotive SE900-5 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Automotive |
| BMC HT12-1027 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Isoplast® 202 LGF40 ETPU | Lubrizol Advanced Materials, Inc. | ETPU | Isoplast® |
| POFEX EP8300S 90M | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |
| Sylvin 7833-85 Blue 8462 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |