RapidCast™ RC-200
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | RapidCast™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5wYsvD_RapidCast-RC-200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RC-200 is a tough, impact resistant elastomer formulated for meter mix dispensing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Cured | 1.05 | g/cm³ | |
| Hardener | 1.07 | g/cm³ | |
| Base Resin | 1.20 | g/cm³ | |
| Molding Shrinkage - Flow | 0.10 to 0.50 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 1140 | MPa | ASTM D790 |
| Flexural Strength | 51.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 89 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 10 to 20 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.50 | Pa·s | |
| 25°C 2 | 0.90 | Pa·s | |
| 25°C 3 | 1.0 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 0.83 to 1.2 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 75 to 85 | ASTM D2240 | |
| Tensile Modulus | 1720 | MPa | ASTM D638 |
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Tensile Elongation at Break | 5.0 | % | ASTM D638 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 150°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| XYRON™ L544V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NYLOY® UB-0010N G35N4N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| DynaMix™ PD5501-TB | Polymer Dynamix | ETFE | DynaMix™ |
| Hylon® N1043STL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Sylvin 9653-50 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |