HIFOR® LF1021
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5wMmGK_HIFORLF1021.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake LF1021 is a butene blown film LLDPE providing excellent mechanical and downgauging performance. This Kosher compliant product is formulated with medium slip, high antiblock, and process aid for high speed blown film extrusions from narrow and wide die gaps. Application/Uses
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 186 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 207 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 35.9 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 24.8 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 670 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 900 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 120 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.4 µm, Blown Film) | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.0 mils fabricated at 2.5:1 BUR, 400° F melt temperature, 9 lbs/hr/in, 100 mil die gap. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 216 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6 MO | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| Moplen HP552K | LyondellBasell Industries | PP Homopolymer | Moplen |
| NuSil R32-2186 | NuSil Technology | Silicone | NuSil |
| BCC Resins BC 7069-1 | BCC Products Inc. | Epoxy | BCC Resins |
| Jackdaw PC DS20WT6701 | Jackdaw Polymers | PC+PBT | Jackdaw PC |