SCHULAMID® 6 MV HI K1893
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5w6xgA_SCHULAMID-6-MV-HI-K1893.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| super high impact modified polyamide 6 compound |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1400 | 400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 35.0 | 22.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.5 | 35 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 100 kJ/m² | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 40.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 210 | -- | °C | ISO 306/A120 |
| -- | 108 | -- | °C | ISO 306/B50 |
| Fill Analysis | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Melt Density (275°C) | 0.890 | -- | ISO 1133 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® N8950 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RTP 1200-75D | RTP Company | TPU, Unspecified | RTP |
| RTP PA66 13 GF BLK | RTP Company | Nylon 66 | RTP |
| ESTACARB 1560 V0 | Cossa Polimeri S.r.l. | PC | ESTACARB |
| Leona™ 90G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |