Diakon® Frost 952 80
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Inc. |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5vSgxp_Diakon-Frost-952-80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon®Frost 952 80 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion. Diakon®The main characteristics of Frost 952 80 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 1.5 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 | |
| Ball Indentation Hardness (H 961/30) | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.4 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 1.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ISO 306/A |
| -- | 101 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 87.3 | % | ASTM D1003 |
| Haze | 89 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 80.0 | °C | |
| Cylinder Zone 1 Temp. | 160 - 240 | °C | |
| Cylinder Zone 2 Temp. | 180 - 250 | °C | |
| Cylinder Zone 3 Temp. | 200 - 250 | °C | |
| Cylinder Zone 4 Temp. | 220 - 260 | °C | |
| Adapter Temperature | 210 - 270 | °C | |
| Die Temperature | 210 - 270 | °C |
| Extrusion instructions |
|---|
| Vent Zone: 220 to 270°CZone 6: 220 to 270°CZone 7: 210 to 270°CZone 8: 210 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC93-80E | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| AQUAFORCE® PA66 G60-01 SCHWARZ | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | AQUAFORCE® |
| Geon™ Vinyl Flexible XV-3766 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Geon™ Vinyl Flexible R125AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| IROGRAN® A 86 E 4486 | Huntsman Corporation | TPU-Polyester | IROGRAN® |