Petrothene® NA963083
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5vFd2e_Petrothene-NA963083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene NA963083 is selected by customers for use in a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA963083 exhibits uniformity, ease of processing and good tensile strength. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 - 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 46 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 10.7 | MPa | ASTM D638 |
| Fracture | 11.4 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 100 | % | ASTM D638 |
| Fracture | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 32 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 32 µm | 179 | MPa | ASTM D882 |
| 1% secant, TD : 32 µm | 221 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 32 µm | 23.4 | MPa | ASTM D882 |
| TD : Yield, 32 µm | 16.5 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 32 µm | 160 | % | ASTM D882 |
| TD : Broken, 32 µm | 480 | % | ASTM D882 |
| Dart Drop Impact (32 µm) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm | 300 | g | ASTM D1922 |
| TD : 32 µm | 180 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 154 - 177 | °C |
| Extrusion instructions |
|---|
| Generally recommended extrusion conditions include a melt temperature range of 310°-350°F (155°-177°C) and a blow-up ratio range of 1.8-2.5:1. Drawdown to gauges below 1.0 mils (<25 microns) is possible at commercial rates when proper techniques are used. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 86MF10 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| Versalloy™ HC 9210-55N | PolyOne Corporation | TPE | Versalloy™ |
| AKROMID® B3 GF 35 black (2196) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Estane® ALR E87A-V TPU | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Estane® |
| Hostacom BJ62A | LyondellBasell Industries | PP Copolymer | Hostacom |