Propafilm™ RXP125
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5uRY8q_Propafilm-RXP125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Peelable Seal Barrier Coated Film Biaxially oriented polypropylene (BOPP) film coated on both sides with an aqueous dispersion of polyvinylidene chloride (PVdC). RXP125 is recommended for use in printed or plain applications in the bakery or confectionery industries. Particularly suitable for V.F.F. applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 121°C, 1 min | 4.0 | % | |
| Flow : 129°C, 1 min | 7.0 | % | |
| Across Flow : 129°C, 1 min | 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 3200 | µm | |
| Seal Strength 1 | 0.14 | N/mm | Internal Method |
| Seal Initiation Temperature 2 | 104 to 146 | °C | Internal Method |
| Oxygen Permeability (25°C, 0% RH) | 0.38 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 3.9 | g/m²/24 hr | ASTM F1770 |
| Yield | 33.6 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | > 100 | ASTM D2457 | |
| Haze 3 | 3.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 2secs; 15psi |
| 2 . | 2secs; 15psi |
| 3 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1383 D TFE 15 | RTP Company | PPS | RTP |
| SABIC® Vestolen P 9421 66409 | Saudi Basic Industries Corporation (SABIC) | PP Random Copolymer | SABIC® Vestolen P |
| ALTECH® PP-H A 4940/100 MR40 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| OnFlex™ HT 40A-3S2131 | PolyOne Corporation | TPE | OnFlex™ |
| Sylvin 8200-85 Blue 8408 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |