Retpol® 1737 HSA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5ta0h6_Retpol-1737-HSA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton 1737 HSA is a 25% mineral filled homopolymer polypropylene compound. It is a very high flow injection moulding grade developed for high gloss appliance/components and stabilized to meet heat ageing requirements of 2000 hours at 130°C and a UL RTI rating of 110°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 41 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.1 to 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 100 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 78 | ||
| Shore D, 15 sec, 3.00 mm | 69 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 27.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 40 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 24 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 380 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 118 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 57.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ OS80 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Ranger PBT PBT-201-G10 202 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Nipol® AR 124 | Zeon Corporation | Rubber | Nipol® AR |
| Formolene® HP4306 | Formosa Plastics Corporation, U.S.A. | HDPE Copolymer | Formolene® |
| LNP™ THERMOCOMP™ ZX06323 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |