Arnite® TV4 220
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5tAPwQ_Arnite-TV4-220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnite® TV4 220 is a Polybutylene Terephthalate (PBT) material filled with 10% glass fiber. It is available in Asia Pacific or Europe. Primary attribute of Arnite® TV4 220: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 | % | |
| Flow | 0.85 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.16 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4600 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 3.9 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | |
| 23°C | 34 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 12 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A USX016W 333 NER | Radici Plastics | Nylon 66 | Radilon® |
| TAIRILAC AE8000 | Formosa Plastics Corporation | ABS | TAIRILAC |
| NOVALENE 7300P | NOVA Polymers, Inc. | TP, Unspecified | NOVALENE |
| SABIC® HDPE B5206 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| OTECH PVC OE9028 - Profile | OTECH Corporation | PVC, Unspecified | OTECH PVC |