LNP™ THERMOCOMP™ QC006 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5snd3h_LNPTHERMOCOMPQC006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP * THERMOCOMP* QC006 is a compound based on PA610 resin containing Carbon Fiber. Added features include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound QC-1006 Product reorder name: QC006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 196 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 15200 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 280 | MPa | ISO 178 |
| -- 4 | 290 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 5(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, unannealed, 64.0mm span | 221 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 205 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 7.4E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 3722J (T2028F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| NuSil CV14-2500 | NuSil Technology | Silicone | NuSil |
| AKROMID® A3 GF 30 S1 natural (3695) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SECCO S1003 | Shanghai SECCO Petrochemical Co., Ltd | PP Homopolymer | SECCO |