PALDUR® R 15 GF 20 Datasheet,PBT,pal plast GmbH-SHANGHAI SUSHENG

Message
PALDUR®R 15 GF 20 is a polybutene terephthalate (PBT) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. PALDUR®R 15 GF 20 applications include electrical/electronic applications, wire and cable, and automotive industries. Features include: flame retardant/rated flame High stiffness high strength chemical resistance Wear-resistant

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Features	Rigidity, high High strength Good chemical resistance Good wear resistance
Uses	Electrical/Electronic Applications Application in Automobile Field Communication Equipment
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.45	g/cm³	ISO 1183
Water Absorption			ISO 62
Saturated, 23°C	0.38	%	ISO 62
Equilibrium, 23°C, 50% RH	0.18	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	7100	MPa	ISO 527-2/1A/1
Tensile Stress (Break, 23°C)	115	MPa	ISO 527-2/1A/5
Tensile Strain (Break, 23°C)	3.5	%	ISO 527-2/1A/5

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	8.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	45	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	214	°C	ISO 306/B50
Melting Temperature (DSC)	225	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index (Solution A)	350	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	HB		UL 94

Additional Information
Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 6700 to 7500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 110 to 120 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 40 to 50 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 7 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 212 to 215 °CDensity, ISO 1183: 1.44 to 1.46 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Additional Information

Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 6700 to 7500 MPaTensile Stress at Break, ISO 527, 23°C, 5 mm/min, Type A: 110 to 120 MPaTensile Strain at Break, ISO 527, 23°C, 5 mm/min, Type A: 3 to 4 %Charpy Unnotched Impact, ISO 179, Type 1, Edgewise, 23°C: 40 to 50 kJ/m²Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 7 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 212 to 215 °CDensity, ISO 1183: 1.44 to 1.46 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.35 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 %

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp SBB3704	Teknor Apex Asia Pacific PTE. LTD.	PVC, Rigid	Sinvicomp
TEKNIFLEX® VPOA12200	Tekni-Films, a div of Tekni-Plex	Film, PVC/PE/EVOH/PE/PCTFE	TEKNIFLEX®
Zytel® PLUS PLSFR95G15DH2 BK269	DuPont Performance Polymers	Nylon, Unspecified	Zytel® PLUS
HAIPLEN H50 X2	Taro Plast S.p.A.	PP Homopolymer	HAIPLEN
Ultramid® A3WG7 HR BK23591	BASF Corporation	Nylon 66	Ultramid®

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	pal plast GmbH
Trademark:	PALDUR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5s8VG7_PALDUR-R-15-GF-20.pdf
PRICE:	Order Products email sales@su-jiao.com