Latamid 6 E02
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5rlV5a_Latamid-6-E02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Toughened. Good impact resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.3 to 1.5 | % | |
| Flow : 2.00 mm | 1.2 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2000 | MPa | |
| 60°C | 450 | MPa | |
| 90°C | 300 | MPa | |
| 120°C | 200 | MPa | |
| 150°C | 150 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact (23°C, 3.20 mm) | 500 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 50.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 55.0 | °C | |
| Vicat Softening Temperature | 175 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 7.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 60.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selar® PA 2072 | DuPont Packaging & Industrial Polymers | Nylon 6 | Selar® PA |
| Amodel® A-1133 HS | Solvay Specialty Polymers | PPA | Amodel® |
| Hostacom EKC 330N E1 G42824 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| LUVOCOM® 1-8895 | LEHVOSS Group | Nylon 66 | LUVOCOM® |
| 3M™ Dyneon™ Fluoroelastomer FT 2481 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |