RTP 1483
| Category: | PESU , Polyethersulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5rd2hq_RTP-1483.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 | % | ASTM D955 |
| Moisture Content | 0.040 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 20700 | MPa | ASTM D638 |
| Tensile Strength | 179 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 1.7 | % | ASTM D638 |
| Flexural Modulus | 17900 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 530 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+5 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 6.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 343 - 377 | °C | |
| Mold Temperature | 135 - 177 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-756S | CHI MEI CORPORATION | ABS | POLYLAC® |
| Retpol® 9015 HSY | PolyPacific Pty. Ltd. | PP Homopolymer | Retpol® |
| XYRON™ DV166 | Asahi Kasei Chemicals Corporation | PPS+PPE | XYRON™ |
| Leona™ 1330G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Perfactory® E-Shell 300 | EnvisionTEC, Inc. | Acrylic, Unspecified | Perfactory® |