Celanex® 5200-2
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5rYsPG_Celanex-5200-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 5200-2 is a 15% fiberglass reinforced polyester with improved surface finish. Celanex 5200-2 contains an internal lubricant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 28 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 38.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 - 0.60 | % | ASTM D955 |
| Flow direction | 0.40 - 0.60 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 91 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 89.6 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.0 | % | ASTM D638 |
| Fracture | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 8000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 185 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.0 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 35 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 7.1 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 216 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 179 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 190 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 65.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 210 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3, ASTM D3418 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+16 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 2 | 19 | kV/mm | ASTM D149 |
| -- | 28 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.70 | ASTM D150 | |
| 100 Hz | 4.30 | IEC 60250 | |
| 1 MHz | 4.00 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 2.0E-3 | ASTM D150 | |
| 100 Hz | 1.1E-3 | IEC 60250 | |
| 1 MHz | 0.019 | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 250 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 235 - 255 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 265°CZone 4 Temperature: 240 to 260°CFeed Temperature: 230 to 250°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VisiJet® M3 Dentcast | 3D Systems | Unspecified | VisiJet® |
| TOTAL Polypropylene PPH 3270 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Xuchuan XWB-335 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| EPO-TEK® TV1003-LV | Epoxy Technology Inc. | PI, TS | EPO-TEK® |
| Infino XP-2165BM | SAMSUNG SDI CO., LTD. | PPS | Infino |