Generic PPE+PS+Nylon - Glass Fiber
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5rPUKz_Generic-PPE-PS-Nylon---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPE+PS+Nylon - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 - 1.37 | g/cm³ | ASTM D792 |
| 23°C | 1.16 - 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.23 - 0.91 | % | ASTM D955 |
| Transverse flow : 23°C | 0.72 - 0.98 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.50 - 0.51 | % | ASTM D570 |
| Saturated, 23°C | 3.7 - 4.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.49 - 1.2 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3570 - 12000 | MPa | ASTM D638 |
| 23°C | 4810 - 12100 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 84.0 - 185 | MPa | ASTM D638 |
| Yield, 23°C | 86.0 - 185 | MPa | ISO 527-2 |
| Fracture, 23°C | 85.4 - 185 | MPa | ASTM D638 |
| Fracture, 23°C | 85.0 - 188 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.0 - 3.1 | % | ASTM D638, ISO 527-2 |
| Fracture, 23°C | 3.0 - 12 | % | ASTM D638 |
| Fracture, 23°C | 2.8 - 7.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3790 - 9400 | MPa | ASTM D790 |
| 23°C | 4540 - 9460 | MPa | ISO 178 |
| Flexural Stress | |||
| 23°C | 144 - 271 | MPa | ISO 178 |
| Yield, 23°C | 141 - 270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 - 11 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 79 - 85 | J/m | ASTM D256 |
| 23°C | 6.9 - 10 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 9.87 - 17.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 214 - 254 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 215 - 241 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 200 - 242 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 210 - 249 | °C | ASTM D1525 |
| -- | 209 - 246 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 2.2E-5 - 5.1E-5 | cm/cm/°C | ASTM E831 |
| Flow | 2.2E-5 - 4.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.4E-5 - 8.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 101 | °C | |
| Drying Time | 3.4 - 3.5 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 40 | % | |
| Rear Temperature | 284 - 285 | °C | |
| Middle Temperature | 287 - 288 | °C | |
| Front Temperature | 290 - 291 | °C | |
| Nozzle Temperature | 293 - 294 | °C | |
| Processing (Melt) Temp | 290 - 294 | °C | |
| Mold Temperature | 98.5 - 99.4 | °C | |
| Back Pressure | 0.853 - 0.862 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPE+PS+Nylon - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP PHC26 | Saudi Basic Industries Corporation (SABIC) | PP Impact Copolymer | SABIC® PP |
| THERMOLAST® K TC0TPZ (Series: GP/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Terlux® 2812 | INEOS Styrolution Group GmbH | MABS | Terlux® |
| Bergadur™ PB40 G15 blue | PolyOne Corporation | PBT | Bergadur™ |
| Moplen HP525J | PolyMirae | PP Homopolymer | Moplen |