UBE Nylon 1013B
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBE Nylon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5rKnMS_UBE-Nylon-1013B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UBE Nylon 1013B is a Polyamide 6 (Nylon 6) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.14 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.4 to 1.5 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.8 | -- | % | |
| Saturation | 11 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 85 | 55 | ||
| R-Scale | 120 | 85 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield | 73.5 | 39.2 | MPa | |
| Break | 63.7 | -- | MPa | |
| Tensile Elongation | ASTM D638 | |||
| Yield | 8.0 | -- | % | |
| Break | 170 | 200 | % | |
| Flexural Modulus | 2550 | 735 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 108 | 39.2 | MPa | ASTM D790 |
| Compressive Strength | 19.6 | 9.80 | MPa | ASTM D695 |
| Shear Strength | 63.7 | 58.8 | MPa | ASTM D732 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -30°C | 39 | -- | J/m | |
| 23°C | 59 | 490 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 175 | -- | °C | |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | |
| Melting Temperature | 215 to 225 | -- | °C | |
| CLTE - Flow | 8.0E-5 | -- | cm/cm/°C | ASTM D696 |
| RTI Elec (0.794 mm) | 65.0 | -- | °C | UL 746 |
| RTI Imp (0.794 mm) | 65.0 | -- | °C | UL 746 |
| RTI Str (0.794 mm) | 65.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | -- | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | |||
| 60 Hz | 3.90 | 9.00 | ||
| 1 MHz | 3.50 | 4.50 | ||
| Dissipation Factor | ASTM D150 | |||
| 60 Hz | 0.010 | 0.10 | ||
| 1 MHz | 0.020 | 0.12 | ||
| Arc Resistance (0.794 mm) | 119 | -- | sec | ASTM D495 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.794 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 230 | °C | |
| Front Temperature | 245 | °C | |
| Nozzle Temperature | 245 | °C | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Pressure | 63.7 | MPa | |
| Back Pressure | 9.80 | MPa | |
| Screw Speed | 100 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ARC-55D-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Wondel® A AM3G3 | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| LEMALLOY® C82HL | Mitsubishi Engineering-Plastics Corp | PPE+Nylon 66 | LEMALLOY® |
| LNP™ THERMOCOMP™ ZX08309 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |
| Maxxam™ H6 GF/30 H Natural | PolyOne Corporation | PP Homopolymer | Maxxam™ |