Sindustris PBT SG3251A
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5qmHil_Sindustris-PBT-SG3251A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PBT SG3251A is a Polybutylene Terephthalate + PET (PBT+PET) material filled with 25% mineral. It is available in Asia Pacific for injection molding. Primary attribute of Sindustris PBT SG3251A: Good Aesthetics. Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 1.2 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4310 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 85.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 105 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 200 | °C | |
| Peak Melting Temperature | 225 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 245 to 255 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 255 to 265 | °C | |
| Nozzle Temperature | 255 to 265 | °C | |
| Processing (Melt) Temp | 255 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA6 2005/43-HF | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| UNIBRITE® UA-1860 | Nippon A&L Inc. | ASA | UNIBRITE® |
| DynaStat® 2359 | Polymer Dynamix | PEBA-Ether | DynaStat® |
| ELASTOSIL® LR 3040/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| LNP™ LUBRICOMP™ Lexan_LF1530A compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |