DOWLEX™ 2631.10UE
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5qTQkq_DOWLEX-2631-10UE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ 2631UE Polyethylene Resin for rotational and injection moulding is specifically designed for applications requiring excellent processability and aesthetics combined with low warpage and good mechanical properties. Processing and Stabilisation: DOWLEX 2631UE™ Polyethylene Resin is fully heat and UV stabilised resulting in a wide processing latitude, good colour retention and long life expectancy. The powder version is named DOWLEX™ 2631.10UE Polyethylene Resin. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (50°C, 100% Antarox, Compression Molded) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 56 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Compression Molded) | 17.8 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 420 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 628 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy 1 | ISO 6603-2 | ||
| -20°C, Rotational Molded | 59.7 to 79.6 | J | |
| 23°C, Rotational Molded | 53.1 to 70.8 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 57.8 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 2 |
| Melting Temperature | 124 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 110 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | Plates of 3-4 mm thickness. |
| 2 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9077-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Trexprene® A64BW-HF | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| WPP PE WPP651 | Washington Penn Plastic Co. Inc. | LLDPE | WPP PE |
| LNP™ LUBRILOY™ RF203H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |
| Hostacom TRC 787N E1 G81493 | LyondellBasell Industries | PP Copolymer | Hostacom |