SOLARENE H616
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Dongbu Hannong Chemical |
| Trademark: | SOLARENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5qEQ3V_SOLARENE-H616.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLARENE H616 is a High Impact Polystyrene product. It is available in Asia Pacific or Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 72 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 32.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 2160 | MPa | ASTM D790 |
| Flexural Strength | 54.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 82.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 102 | °C | ASTM D1525 1 |
| -- | 95.0 | °C | ASTM D1525 2 |
| RTI Elec | UL 746 | ||
| 1.59 mm | 50.0 | °C | |
| 3.17 mm | 50.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.59 mm | 50.0 | °C | |
| 3.17 mm | 50.0 | °C | |
| RTI Str | UL 746 | ||
| 1.59 mm | 50.0 | °C | |
| 3.17 mm | 50.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 | |
| Arc Resistance | ASTM D495 | ||
| 1.59 mm | PLC 7 | ||
| 3.17 mm | PLC 7 | ||
| Comparative Tracking Index (CTI) | UL 746 | ||
| 1.59 mm | PLC 1 | ||
| 3.17 mm | PLC 1 | ||
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.59 mm | PLC 3 | ||
| 3.17 mm | PLC 3 | ||
| High Voltage Arc Tracking Rate (HVTR) | UL 746 | ||
| 1.59 mm | PLC 0 | ||
| 3.17 mm | PLC 0 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.59 mm | PLC 3 | ||
| 3.17 mm | PLC 3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm, ALL | HB | ||
| 3.17 mm, ALL | HB |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| 2 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® A MV 14 FR 1 | A. Schulman Europe | PBT | SCHULADUR® |
| Nylene® BS-700-A | Custom Resins Group | Nylon 6 | Nylene® |
| Arnitel® UM551-V | DSM Engineering Plastics | TPC-ES | Arnitel® |
| Hybrid S466 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| LNP™ FARADEX™ ZX93134 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ FARADEX™ |