SABIC® PP 513MNK10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5q0NBy_SABIC-PP-513MNK10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This very high flow grade shows a medium impact resistance, even at low temperatures, combined with high stiffness. It is used for high speed processing of thin walled packaging articles like margarine tubs, ice cream containers and flowerpots. SABIC® PP 513MNK10 is also suited for moulding of caps and closures, toys and housewares. This grade is also available with an anti-static additive package. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 70 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 93 | ASTM D785 | |
| Shore Hardness (Shore D) | 62 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1400 | MPa | ASTM D638 |
| -- | 1350 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 25.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Notched Izod Impact | |||
| 0°C | 50 | J/m | ASTM D256A |
| 23°C | 60 | J/m | ASTM D256A |
| 0°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 75.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Veroplas K18 | PlastxWorld Inc. | Acrylic (PMMA) | Veroplas |
| Eleme HFW00346 | Eleme Petrochemical Company Ltd | HDPE | Eleme |
| Vipel® F010-H2O-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| 3M™ Dyneon™ PTFE Compound FM 2370079 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| ESTOPLAST XU 150HG BB01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |