RTP 901 TFE 10 Z
| Category: | PSU , Polysulfone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5pxnmb_RTP-901-TFE-10-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - PTFE Lubricated - FDA Compliant Ingredients |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Moisture Content | 0.15 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4480 | MPa | ASTM D638 |
| Tensile Strength | 79.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 to 4.0 | % | ASTM D638 |
| Flexural Modulus | 4480 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 480 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 177 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | -31.7 | °C | |
| Processing (Melt) Temp | 332 to 371 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Injection Pressure | 68.9 to 124 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® G16S | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| TAIRILAC AX4100 | Formosa Plastics Corporation | ABS | TAIRILAC |
| NEXUS PP RPP2C | Nexus Resin Group, LLC. | PP Random Copolymer | NEXUS PP |
| Dyna-Purge® C | Dyna-Purge, division of Shuman Plastics | Proprietary | Dyna-Purge® |
| Karina BLACK PVC COMPOUND 771-48/ 1-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |