EMERGE™ PC 8830-5 LT
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5pgPoo_EMERGEPC88305LT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8830-5 LT Advanced Resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based flame retardant, designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and heat resistant properties, ensuring longer sustained aesthetics and mechanical resistance to the applications. EMERGE ™ PC 8830-5LT has a UL 94 V-0 rating at 1.0 mm and contains mould release agent and UV stabilizer Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.70 | % | ISO 294-4 |
| Flow | 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield, 3.20mm, injection molding | 64.0 | MPa | ISO 527-2/50 |
| Fracture, 3.20mm, injection molding | 59.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 3.20mm, injection molding | 6.3 | % | ISO 527-2/50 |
| Fracture, 3.20mm, injection molding | 110 | % | ISO 527-2/50 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2240 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, Injection Molded) | 13 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 136 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 128 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A120 |
| -- | 143 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.0 mm 1 | V-0 | UL 94 | |
| 2.5 mm 2 | 5VB | UL 94 | |
| 3.0 mm 3 | 5VA | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm 4 | 800 | °C | IEC 60695-2-12 |
| 1.5 mm 5 | 960 | °C | IEC 60695-2-12 |
| 2.0 mm 6 | 960 | °C | IEC 60695-2-12 |
| 3.0 mm 7 | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature 8 | IEC 60695-2-13 | ||
| 1.0 mm | 825 | °C | IEC 60695-2-13 |
| 1.5 mm | 825 | °C | IEC 60695-2-13 |
| 2.0 mm | 825 | °C | IEC 60695-2-13 |
| 3.0 mm | 825 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Transmittance | |||
| 1000 µm | 90.0 | % | |
| 2000 µm | 88.0 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 280 - 310 | °C | |
| Front Temperature | 290 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Mold Temperature | 60 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 4 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4077 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Quadrathane™ ALC-85A | Biomerics, LLC | TPU-PC | Quadrathane™ |
| Gallonprene® GP420-3003 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KEBAFORM® C 50.0 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Sylvin 9604-80 Clear Black 2106 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |