EPO-TEK® 301-2FL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5oZdxQ_EPO-TEK-301-2FL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 301-2FL is a two component optical, medical, and semiconductor grade epoxy resin. It is a more flexible version of EPO-TEK® 301-2. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 105 | ppm | |
| K+ | 19 | ppm | |
| Na+ | 58 | ppm | |
| NH4+ | 8 | ppm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 325 | °C | TGA |
| Die Shear Strength - >10 kg (23°C) | 23.4 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 150 | °C | |
| Intermittent | -55 to 250 | °C | |
| Storage Modulus | 1.05 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.50 | % | |
| 250°C | 0.96 | % | |
| 300°C | 3.5 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 45.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.6E-5 | cm/cm/°C | |
| -- 3 | 2.1E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.512 | ||
| Transmittance | |||
| 400 to 1000 nm | > 99.0 | % | |
| 1000 to 1600 nm | > 97.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 35 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 0.888 | g/cm³ | |
| Part A | 1.06 | g/cm³ | |
| Viscosity 7(23°C) | 0.10 to 0.20 | Pa·s | |
| Curing Time (80°C) | 3.0 | hr | |
| Pot Life | 600 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 70 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 3.54 | ||
| Volume Resistivity | > 6.0E+11 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.013 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M6112 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| VAMPLEN A 0023 C V2 | Vamp Tech | PP Copolymer | VAMPLEN |
| NuSil R32-2186 | NuSil Technology | Silicone | NuSil |
| Chemical Resources PMMA1400 | Chemical Resources, Inc. | Acrylic (PMMA) | Chemical Resources |
| ALCOM® PA66 910/1 NU SV1057-03MCF | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |