Category: | HDPE , High Density Polyethylene |
Manufacturer: | FKuR Kunststoff GmbH |
Trademark: | Terralene® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | 5oUPXT_Terralene-WF-3516.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
High desnity polyethylene with narrow molar mass distribution, containing a low amount of wood fibers and functional additives. Recommended for the production of injection moulded articles. |
General Information | |
---|---|
Filler / Reinforcement |
|
Additive |
|
Features |
|
Forms |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density 1 | 1.01 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 11 to 13 | g/10 min | ISO 1133 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 1310 | MPa | ISO 527-2 |
Tensile Stress | ISO 527-2 | ||
Yield | 23.0 | MPa | |
Break | 22.5 | MPa | |
Tensile Strain | ISO 527-2 | ||
Yield | 9.0 | % | |
Break | 10 | % | |
Flexural Modulus | 1270 | MPa | ISO 178 |
Flexural Stress (3.5% Strain) | 22.0 | MPa | ISO 178 |
Flexural Strain at Break | No Break | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength | 3.1 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength | 15 | kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Melting Temperature | 130 to 145 | °C | ISO 3146 |
Note Message | |
---|---|
1 . | Measured on injection moulded specimen |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
SHIN-A SE-80 | SHIN-A T&C | Epoxy | SHIN-A |
Sinpolene HFR8224 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
Starex NH-1907 | SAMSUNG SDI CO., LTD. | PS (HIPS) | Starex |
Unichem 9500 | Colorite Polymers | PVC, Unspecified | Unichem |
Aurora PVC AP2144 Series 050902 | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |