Maxxam™ PPC-40G Black
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Maxxam™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5myr88_Maxxam-PPC-40G-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium carbonate, glass and talc to provide a desired balance of properties including stiffness, durability, impact resistance and heat resistance. Custom grades are available with features such as UV stabilizers, heat stabilizers, custom color, high impact, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Specific Volume | 0.820 | cm³/g | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 6550 | MPa | ASTM D790 |
| Flexural Strength | 88.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 53 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed, 3.18 mm) | 156 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 16.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene XSene® HDPE XRC20 Orange | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| ULTZEX™ 20100J | Prime Polymer Co., Ltd. | LLDPE | ULTZEX™ |
| Braskem PP C706-21NAHP | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| FHR EPS R-MER II® 5627 (1.75 lb/ft³) | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| LUVOCOM® 70-9172/BL | LEHVOSS Group | PK | LUVOCOM® |