DESLON™ 6 DSC101M4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DESCO Co., Ltd. |
| Trademark: | DESLON™ 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5lsZ6b_DESLON-6-DSC101M4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Descriptions: DESLON™ DSC101M4 is Polyamide6 Mineral Filler 20% filled reinforced resin. It provides good mechanical properties and dimensions stability. Applications: DESLON™ DSC101M4 is one of the most-used for good surface appearance and good dimensions stability goods etc. such as Electronic & Automotive Parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 - 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 4900 | MPa | ASTM D790 |
| Flexural Strength | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 205 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 - 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Nozzle Temperature | 255 - 270 | °C | |
| Processing (Melt) Temp | 255 - 270 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Speed: 30 to 60%Pressure 1st: 30 to 70%Pressure 2nd: 30 to 70Holding Pressure: 10 to 30% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-265 | Ravago Manufacturing Americas, LLC | LLDPE | Ravago Compounds |
| SABIC® LLDPE 726QE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| COBITECH 2 | M&G Gruppo Mossi & Ghisolfi | PET | COBITECH |
| Karina WHITE PVC COMPOUND -E 600D10/ 1 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® ECO T 3240 000000 | LANXESS Corporation | PBT+PET | POCAN® |