POLYCOMPO PE FL60
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | POLYCOMPO Co.,Ltd. |
| Trademark: | POLYCOMPO PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5k4IQY_POLYCOMPO-PE-FL60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| POLYCOMPO PE FL60 is a Low Density Polyethylene product. It can be processed by injection molding and is available in Asia Pacific. Typical application: Caps/Lids/Closures. Primary characteristic: high flow. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 70 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Injection Molded) | 45 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, Injection Molded) | 18.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Injection Molded) | 200 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 130 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -20.0 | °C | ASTM D746A, ISO 974 |
| Vicat Softening Temperature | 76.0 | °C | ASTM D1525, ISO 306 |
| Peak Crystallization Temperature (DSC) | 102 | °C | ASTM D3418, ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAPEEK GLD 140 FG blue | Röchling Sustaplast SE & Co. KG | PEEK | SUSTAPEEK |
| Tufel® II 94705 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| APEX® 3300-90NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Hylon® N1040MGL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina COMP. PVC GRAY -E 842-18/106-Y-RT-POWDER | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |