LNP™ LUBRICOMP™ KP004AXP compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5inKa7_LNP-LUBRICOMP-KP004AXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KP004AXP is a compound based on Acetal Homopolymer containing PTFE, Silicone. Added features include Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound KL-4540D Product reorder name: KP004AXP |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 3.0 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 43.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 13 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress | 61.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.16 | ||
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 85.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.2E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DENILUB N 00U 0Si | Vamp Tech | Nylon 6 | DENILUB |
| Eltex® HD5211EA-B | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| LITEN BB 38 S | UNIPETROL RPA | PE Copolymer | LITEN |
| Karina BLUE COLOR CONCENTRATE 06/30-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ XHT1141 resin | SABIC Innovative Plastics | PC | LEXAN™ |