Sarlink® TPE EE-2740D NAT
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5iTseR_Sarlink-TPE-EE-2740D-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE EE-2740DN is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Sarlink®The main features of TPE EE-2740DN are:
Sarlink®The typical application field of TPE EE-2740DN is: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.9 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 1 second, injection molding | 42 | ASTM D2240 | |
| Shore D, 5 seconds, injection molding | 37 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 148 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| Transverse flow : 100% strain | 5.90 | MPa | ASTM D412 |
| Flow : 100% strain | 6.70 | MPa | ASTM D412 |
| Tensile Strength | ASTM D412 | ||
| Transverse flow : Fracture | 8.20 | MPa | ASTM D412 |
| Flow : Fracture | 9.00 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Transverse flow : Fracture | 590 | % | ASTM D412 |
| Flow : Fracture | 520 | % | ASTM D412 |
| Tear Strength - Across Flow | 62.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 22 hr | 56 | % | ASTM D395 |
| 70°C, 22 hr | 80 | % | ASTM D395 |
| 90°C, 70 hr | 92 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | ISO 188 | ||
| 110°C, 1008 hr | 6.1 | % | ISO 188 |
| 125°C, 168 hr | 9.8 | % | ISO 188 |
| Changes in tensile stress upon fracture in air- Transverse flow | ISO 188 | ||
| 110°C, 1008 hr | -15 | % | ISO 188 |
| 125°C, 168 hr | -18 | % | ISO 188 |
| Change in Shore Hardness in Air | ISO 188 | ||
| 110°C, 1008 hr | -1.2 | ISO 188 | |
| Support a, 125°C, 168 hr | 0.0 | ISO 188 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 66 | mm/min | ISO 3795 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 454 | Pa·s | ASTM D3835 |
| Additional Information |
|---|
| 热变形温度 (0.45 MPa) - ASTM D648 = 58氙气灯老化 2500千焦 (SAE J-1960) = 1.48 DELTA E多轴向冲击，-40C 焦耳加纳德冲击，-30C英寸-磅 (焦) = 256 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 MF 30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Tufpet PBT S1040B | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| NEXT PCR PA66 GM35-300PCR | NEXT Specialty Resins, Inc. | Nylon 66 | NEXT PCR |
| Hanwha Total PP TB52 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina GRAY PVC COMPOUND 853-18/190-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |