Borealis PE FG5224
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5hczAh_Borealis-PE-FG5224.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FG5224 is a Butene Linear Low Density Polyethylene for Film Extrusion. Includes Antioxidant, Anti-block and Medium Slip additives. This grade is developed for production of lamination film. FG5224 has good heat sealing properties and hot tack strength. By mixing with FG5223 any desired level of friction can be obtained. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic) | 0.10 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| secant modulus | ASTM D882A | ||
| MD : 70 µm | 145 | MPa | ASTM D882A |
| TD : 70 µm | 165 | MPa | ASTM D882A |
| Tensile Strength | ISO 527-3 | ||
| MD : 70 µm | 29.0 | MPa | ISO 527-3 |
| TD : 70 µm | 28.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 70 µm | 800 | % | ISO 527-3 |
| TD : Break, 70 µm | 1000 | % | ISO 527-3 |
| Dart Drop Impact (70 µm) | 260 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm | 2.0 | N | ISO 6383-2 |
| TD : 70 µm | 9.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 122 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (70.0 µm) | 100 | ASTM D2457 | |
| Haze (70.0 µm) | 10 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 - 230 | °C |
| Extrusion instructions |
|---|
| Blow Up Ratio: 2:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP2B40 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| RAMTOUGH PZ322G2 | Polyram Ram-On Industries | PC | RAMTOUGH |
| SAXALAC™ 310A | SAX Polymers | ABS | SAXALAC™ |
| ALKAMIX™ MB6002 | Qenos Pty Ltd | LLDPE | ALKAMIX™ |
| Elastamax™ HTE 3060 | PolyOne Corporation | PVC+NBR | Elastamax™ |