LNP™ LUBRICOMP™ UCL36S compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5hKpi6_LNPLUBRICOMPUCL36Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP UCL36S is a compound based on Polyphthalamide resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Heat Stabilized, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound UCL-4036 HS Product reorder name: UCL36S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 20100 | MPa | ASTM D638 |
| Tensile Strength | |||
| Fracture | 216 | MPa | ASTM D638 |
| Fracture | 214 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.6 | % | ASTM D638 |
| Fracture | 1.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 18800 | MPa | ASTM D790 |
| -- | 22700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 324 | MPa | ASTM D790 |
| -- | 334 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.36 | ASTM D3702 Modified | |
| With Self-Static | 0.27 | ASTM D3702 Modified | |
| Wear Factor - Washer | 16.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 8.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 940 | J/m | ASTM D4812 |
| 23°C 3 | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 279 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 310 - 321 | °C | |
| Middle Temperature | 316 - 327 | °C | |
| Front Temperature | 327 - 338 | °C | |
| Processing (Melt) Temp | 316 - 332 | °C | |
| Mold Temperature | 149 - 171 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3030JFX3 | UBE Industries, Ltd. | Nylon 12 | UBESTA |
| Hostalen CRP 100 S blue | LyondellBasell Industries | HDPE | Hostalen |
| INLUBE POMCGF20TF15 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INLUBE |
| Karina BLACK PVC COMPOUND TR-601D48/1-Y-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8474-80 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |