Ferro PP TPP20AF01HB YELLOW
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gutUh_Ferro-PP-TPP20AF01HB-YELLOW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP TPP20AF01HB YELLOW is a polypropylene homopolymer (PP Homopoly) material, which contains 23% talc filler. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. The main characteristics of Ferro PP TPP20AF01HB YELLOW are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 32.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 20 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 2210 | MPa | ASTM D790 |
| Tangent : 23°C | 2650 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 50.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 480 | J/m | ASTM D4812 |
| Dart Drop Impact (23°C) | 2.26 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 121 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 68.3 | °C | ASTM D648 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TPSF-FRG10 | Polymer Resources Ltd. | PBT | PRL |
| TUFNYL® SST 20 BLACK | SRF Ltd. | Nylon 6 | TUFNYL® |
| Daelim Po1y® LH860 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Hylon® N1240MGHL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Karina IVORY PVC COMPOUND -E 602D35/ 1-A-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |