GLAMIDE® T-808-02
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5grGHW_GLAMIDE-T-808-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®T-808-02 is a polyamide 6 (nylon 6) product,. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.18 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 40 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.40 - 0.80 | -- | % | ASTM D955 |
| 3.00 mm | 1.0 - 1.3 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 1.3 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 3.0 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 100 | 90.0 | MPa | ASTM D638 |
| Yield, 23°C | 75.0 | 40.0 | MPa | ASTM D638 |
| Yield, 80°C | 32.0 | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 6.0 | 15 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 5500 | 5100 | MPa | ASTM D790 |
| 23°C | 3300 | 1300 | MPa | ASTM D790 |
| 80°C | 1000 | 500 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 145 | 120 | MPa | ASTM D790 |
| Yield, 23°C | 100 | 45.0 | MPa | ASTM D790 |
| Yield, 80°C | 42.0 | 26.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 80.0 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 30 | 45 | J/m | ASTM D256 |
| 23°C | 43 | 180 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 190 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 84.0 | -- | °C | ASTM D648 |
| CLTE - Flow | 7.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 5.20 | -- | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.080 | -- | ASTM D150 | |
| Arc Resistance | 120 | 105 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Volume Resistivity, ASTM D257: 1e9 to 1e10 ohm-mComparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Pressure | 30.0 - 45.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sympoxy™ 18752 | Hapco Inc. | Epoxy | Sympoxy™ |
| ACCUTECH™ HP0336M40CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| King Pearl® G-L | Loyal Chemical | PS (EPS) | King Pearl® |
| INEOS PP H07G-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |
| ULTEM™ 2110 resin | SABIC Innovative Plastics | PEI | ULTEM™ |