PENTALLOY BTA H UV black 9040
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTALLOY BTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gmufL_PENTALLOYBTAHUVblack9040.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT-ASA alloy, unreinforced, heat stabilised, special coloration, high UV resistance |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.60 | % | ISO 294-4 |
| Flow | 0.50 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | ISO 527-2/50 |
| Fracture | > 10 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 85.0 | °C | ISO 75-2/A |
| Melting Temperature | 222 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.090 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 250 - 275 | °C | |
| Middle Temperature | 255 - 280 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Processing (Melt) Temp | 245 - 285 | °C | |
| Mold Temperature | 60 - 100 | °C | |
| Injection Pressure | 45.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYLON® 235NL | Tyne Plastics LLC. | Nylon 6 | TYLON® |
| Fainplast PVC GS 38/T | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Globalprene® 5516 | Lee Chang Yung Chemical Industry Corp. | SIS | Globalprene® |
| Petrothene® GS707062 | LyondellBasell Industries | LLDPE | Petrothene® |
| ESTOPLAST XU 6250NN11 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |