Radilon® A LX 14080K 100 M NAT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gfKZR_Radilon-A-LX-14080K-100-M-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 medium-high viscosity injection moulding and extrusion grade. Heat stabilized. Natural colour. Suitable for moulding parts with high thickness requiring good impact resistance. Typically used for railway applications, such as rail insulators. ISO 1043 : PA66-T |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 195 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 80.0 | -- | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.5 | -- | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 50 | -- | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2980 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 115 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | -- | kJ/m² | ISO 179/1eA |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 270 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PP TL603 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Network Polymers PS CPS 80-1200B- BEADS | Network Polymers, Inc. | PS (GPPS) | Network Polymers PS |
| 3M™ Dyneon™ Fluoroplastic PVDF 60120000 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| Hostacom TYC727D | LyondellBasell Industries | TPO (POE) | Hostacom |
| Karina CLEAR PVC COMPOUND 75/200-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |