ColorFast® NY2115
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LTL Color Compounders, Inc. |
| Trademark: | ColorFast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gBLSx_ColorFast-NY2115.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super tough nylon 6,6 with excellent chemical resistance and ductility |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/5.0 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 52.4 | MPa | |
| Break | 46.9 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 18 | % | |
| Break | 70 | % | |
| Flexural Modulus 3 | 2000 | MPa | ASTM D790 |
| Flexural Strength 4 | 72.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 71.1 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Shot Size | 30 to 60 | % | |
| Rear Temperature | 249 to 282 | °C | |
| Middle Temperature | 254 to 282 | °C | |
| Front Temperature | 254 to 282 | °C | |
| Nozzle Temperature | 249 to 277 | °C | |
| Processing (Melt) Temp | 268 to 293 | °C | |
| Mold Temperature | 37.8 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 60 to 120 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GA-3680 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Moplen EPC40R | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| Celstran庐 POM-GF35-04 AF3001 | Celanese Corporation | Acetal (POM) Copolymer | Celstran® |
| Karina CLEAR PVC COMPOUND 75/202 (MP-1.0) (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 230 01 HB | LOXIM Industries Private Limited | PBT | LOXIM |