Formolene® HB5202B2
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5gA4Ne_Formolene-HB5202B2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Formolene HB5202B2 is designed for applications requiring excellent stiffness, impact strength, and excellent stress crack resistance. It may be used as a blow molding resin or sheet extrusion thermoforming resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| Compression Molded, F50 | 50.0 | hr | ASTM D1693B |
| 100% Igepal, Compression Molded, F50 | 50.0 | hr | ASTM D1693A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 600 | % | ASTM D638 |
| Flexural Modulus (Compression Molded) | 1310 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -118 | °C | ASTM D746 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chemlon® E-66 GF15 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| ColorFast® FRPS200 | LTL Color Compounders, Inc. | PS (HIPS) | ColorFast® |
| Forprene® 6NE001A80 | SO.F.TER. SPA | TPV | Forprene® |
| Edgetek™ PC-10GF/000 BLK007 | PolyOne Corporation | PC | Edgetek™ |
| LUVOCOM® 1/GF/30/TF/15/HS/BK | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |