SABIC® PP QR6701K

Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	SABIC Americas, Inc.
Trademark:	SABIC® PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5g0gzP_SABIC-PP-QR6701K.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Provisional - PP random co-polymer for Injection moulding

QR6701K is specially developed for producing injection molded & ISBM articles with very high clarity at low processing temperatures and also has better impact properties than homo PP counterparts. This grade contains advance clarifier & anti-static agent.

QR6701K has following features:

Consistent processability

Good stiffness

Exceptional clarity

Lower energy consumption & less cycle time due to low processing temperatures

Typical Applications
QR6701K can be used for clear houseware & packaging items, appliances, caps & closures, lids and bottles (ISBM).

General Information
Additive	Antistatic Clarifier
Features	Antistatic Fast Molding Cycle Food Contact Acceptable Good Impact Resistance Good Processability Good Stiffness High Clarity Random Copolymer
Uses	Appliances Bottles Caps Closures Household Goods Lids Packaging Transparent Parts
Appearance	Clear/Transparent
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity ¹	0.905	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	10	g/10 min	ASTM D1238
Molding Shrinkage - Flow	1.2 to 2.0	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale, Injection Molded)	94		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield, Injection Molded)	28.0	MPa	ASTM D638
Tensile Elongation (Yield, Injection Molded)	12	%	ASTM D638
Flexural Modulus - 1% Secant (Injection Molded)	1050	MPa	ASTM D790A

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, Injection Molded)	85	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	83.0	°C	ASTM D648
Vicat Softening Temperature	128	°C	ASTM D1525 ²

Injection	Nominal Value	Unit
Rear Temperature	190 to 220	°C
Middle Temperature	190 to 220	°C
Front Temperature	190 to 220	°C
Mold Temperature	15.0 to 40.0	°C

Note Message
1 .	23°C
2 .	Rate B (120°C/h)

Resin Grade	Manufacturer	Category	Trademark
THERMOLAST® K TC6UVZ (Series: UV/AP)	KRAIBURG TPE	TPE	THERMOLAST® K
AVALON® 60 DB	Huntsman Corporation	TPU-Polyester	AVALON®
APEX® 1008	Teknor Apex Company	PVC, Flexible	APEX®
Lupoy® 1301-12	LG Chem Ltd.	PC	Lupoy®
POLYblend PC/ABS 45FS	Polykemi AB	PC+ABS	POLYblend