UBE Nylon 5033 FDX57 Datasheet,Nylon 66/6,UBE Engineering Plastics, S.A.-SHANGHAI SUSHENG

Message
UBE NYLON 5033 FDX57 is a high viscosity, nucleated Polyamide 6/6.6 copolymer. It is most suitable for water-cooled blown film production. Typical application is for sausage casing and shrink bags.

General Information
Additive	Nucleating agent
Features	Nucleated Highlight Workability, good Definition, high Compliance of Food Exposure Viscosity, High
Uses	Films Bags cast film
Agency Ratings	European food contact, not rated
Forms	Particle
Processing Method	Blow film cast film

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	1.0	ASTM D1894
With Self-Static	1.0	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	400	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	24.0	MPa	ASTM D882
Fracture, extruded film	115	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	650	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	196	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	155		ASTM D523
Haze	< 0.50	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 24 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.08Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 85/15Water Vapor Permeability, JIS Z0208: 125 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 10.0 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Coefficient of Friction, ASTM D1894, Dynamic: >1Coefficient of Friction, ASTM D1894, Static: >1Oxygen Permeability, ASTM D3985: 24 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.08Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 85/15Water Vapor Permeability, JIS Z0208: 125 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 10.0 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <5 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <5 hole/0.04 m²

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5fp4GQ_UBE-Nylon-5033-FDX57.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 2283 HF	RTP Company	PEEK	RTP
Premi-Glas® 1201-20	Premix, Inc.	TS, Unspecified	Premi-Glas®
Hostaform® FK 1:25	Celanese Corporation	Acetal (POM) Copolymer	Hostaform®
Hostalen CRP 100 S brown	LyondellBasell Industries	HDPE	Hostalen
Braskem PE HDB0763	Braskem IDESA	HDPE	Braskem PE