PRL PEI-G10
| Category: | PEI , Polyether Imide |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5fav83_PRL-PEI-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PEI-G10 is a Polyether Imide (PEI) product filled with 10% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 5.0 to 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.21 | % | |
| Equilibrium, 23°C | 1.2 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.18 mm) | 4550 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 114 | MPa | |
| Break, 3.18 mm | 114 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 5100 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.18 mm) | 480 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (23°C, 3.18 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 207 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 204 | °C | |
| Vicat Softening Temperature | 221 | °C | ASTM D1525 1 |
| CLTE - Flow (-20 to 150°C) | 3.2E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 105 | °C | |
| 3.00 mm | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.59 mm, in Oil) | 27 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 3.50 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 1.4E-3 | ||
| 2.00 GHz | 4.6E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm, ALL | V-0 | ||
| 3.00 mm, ALL | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 143 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Rear Temperature | 332 to 399 | °C | |
| Middle Temperature | 338 to 399 | °C | |
| Front Temperature | 343 to 399 | °C | |
| Processing (Melt) Temp | 338 to 399 | °C | |
| Mold Temperature | 107 to 177 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J226E | Prime Polymer Co., Ltd. | PP Random Copolymer | Prime Polypro™ |
| Scolefin 53 G 10-1 | Ravago Group | PP Homopolymer | Scolefin |
| VITAMIDE® AR33BK9002 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Lushan RF1000 | Guangzhou Lushan New Materials Co., Ltd | PE, Unspecified | Lushan |
| Sylvin 6920X08 Grey 9550 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |