Luran® HH-120
| Category: | AMSAN , Alphamethylstyrene Acrilonitrile |
| Manufacturer: | Styrolution |
| Trademark: | Luran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5f9isD_Luran-HH-120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran HH-120 is a grade of AMSAN with high heat resistance and improved mechanical strength. It is suitable for injection molding and extrusion applications and can be used as a modifier for high heat ABS and PVC. For TDS and further information about the specialty piano black versions of Luran HH-120 including Styrolution's latest SPF50 UV protection technology please contact the Styrolution Infopoint. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.60 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.30 to 0.70 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ||
| Ball Indentation Hardness | 175 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 79.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 21 | kJ/m² | |
| 23°C | 20 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.17 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 3.00 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.0E-3 | ||
| 1 MHz | 7.0E-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.567 | ISO 489 | |
| Transmittance (550 nm) | > 89.0 | % | ASTM D1003 |
| Haze | < 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 270 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Note Message | |
|---|---|
| 1 . | With external lubricant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPHFGC-1 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Hapflex™ 573 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| KEBAFORM® C 25.0 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| Elastocon® 2840 | Elastocon TPE Technologies | TPE | Elastocon® |
| LUVOCOM® 46/CF/15 | LEHVOSS Group | Nylon 46 | LUVOCOM® |