DynaMix™ XP-5529

Category:	TP, Unspecified , Thermoplastic
Manufacturer:	Polymer Dynamix
Trademark:	DynaMix™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	5f1oH8_DynaMix-XP-5529.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

High Temperature Polymer

Features:

Good Processing

Excellent Chemical Resistance

Low Temperature Properties

Applications:

Wire and Cable

Industrial

Automotive

General Information
Features	Good Chemical Resistance Good Impact Resistance Good Processability
Uses	Automotive Applications Industrial Applications Wire & Cable Applications
Processing Method	Injection Molding

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	62.1	MPa
Break	61.4	MPa
Tensile Elongation			ASTM D638
Yield	9.0	%
Break	15	%
Flexural Modulus	2210	MPa	ASTM D790
Flexural Strength	77.2	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm)	350	J/m	ASTM D256

Injection	Nominal Value	Unit
Drying Temperature	76.7 to 82.2	°C
Drying Time	2.0 to 4.0	hr
Rear Temperature	277 to 293	°C
Middle Temperature	288 to 304	°C
Front Temperature	299 to 316	°C
Nozzle Temperature	299 to 316	°C
Processing (Melt) Temp	299 to 316	°C
Mold Temperature	121 to 149	°C
Injection Pressure	68.9 to 138	MPa
Injection Rate	Moderate
Back Pressure	0.345 to 0.689	MPa
Screw Speed	40 to 70	rpm
Clamp Tonnage	5.5 to 8.3	kN/cm²

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8954-92 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
BorECO™ BA2000	Borealis AG	PP Copolymer	BorECO™
Karina CLEAR PVC COMP. -E 70/236-DA-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
PARAPET GH-S	Kuraray Co., Ltd.	Acrylic (PMMA)	PARAPET
LNP™ THERMOCOMP™ Lexan_LGK5030 compound	SABIC Innovative Plastics Asia Pacific	PC	LNP™ THERMOCOMP™