LACEA® H-100J (Stretched)
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Mitsui Chemicals, Inc. |
| Trademark: | LACEA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5eV4C6_LACEA-H-100J-Stretched-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LACEA®H-100J (Stretched) is a polylactic acid (PLA) material,. This product is available in the Asia-Pacific region and is processed by blow molding or injection molding. LACEA®The main characteristics of H-100J (Stretched) are: environmental protection/green. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.26 | g/cm³ | ASTM D1505 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| L scale | 84 | ASTM D785 | |
| Class r | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 68.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3700 | MPa | ASTM D790 |
| Flexural Strength | 98.0 | MPa | ASTM D790 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus - MD | 3850 | MPa | ASTM D882 |
| Tensile Strength - MD (Yield) | 105 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break) | 140 | % | ASTM D882 |
| Elmendorf Tear Strength - TD | 2.7 | g | ASTM D1922 |
| Water Vapor Transmission | 160 | g/m²/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 55.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 58.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.0 µm) | 93 | % | ASTM D1003 |
| Additional Information |
|---|
| The value listed as Oxygen Permeability, ASTM D3985, was tested in accordance with JIS-K7126.The value listed as Water Vapor Transmission, ASTM E96, was tested in accordance with JIS-K7129.The value listed as Density, ASTM D1505, was tested in accordance with JIS-K6758.The value listed as Tensile Strength @ Yld MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Elongation @ Break MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Secant Modulus MD, ASTM D882, was tested in accordance with JIS-C2318.The value listed as Elmendorf Tear St TD, ASTM D1922, was tested in accordance with JIS-K7128.The value listed as Haze, ASTM D1003, was tested in accordance with JIS-K6714.Oxygen Permeability, JIS-K7126. 23°C, Method A: 450 cm³/m²/day/atmNitrogen Permeability, JIS-K7126. 23°C, Method A: 80 cm³/m²/day/atmCO2 Permeability, JIS-K7126. 23°C, Method A: 1700 cm³/m²/day/atmHeat Shrinkage, 100°C, 1hr, MD: 2.4%Heat Shrinkage, 100°C, 1hr, TD: 0.9% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 150 - 160 | °C | |
| Middle Temperature | 160 - 180 | °C | |
| Front Temperature | 170 - 190 | °C | |
| Nozzle Temperature | 160 - 180 | °C | |
| Mold Temperature | 20.0 - 30.0 | °C |
| Injection instructions |
|---|
| Cooling Time: 30 to 40 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V938 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Nypol® PA A3 G20 NTLA010 NR401 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| ASI POLYETHYLENE LP 551-01 | A. Schulman Inc. | HDPE Copolymer | ASI POLYETHYLENE |
| Iupilon® GSH2020DF | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| NEOFLON™ M-300P | DAIKIN AMERICA, INC. | PCTFE | NEOFLON™ |