RTP 205 TFE 10 SI

Category: Nylon 66 , Polyamide 66
Manufacturer: RTP Company
Trademark: RTP
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: 5eUInb_RTP-205-TFE-10-SI.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
Warning: The status of this material is 'Commercial: Limited Issue'

The data for this material has not been recently verified.
Please contact RTP Company for current information prior to specifying this grade.

-Preliminary Product Data per RTP Co.-
General Information
Filler / Reinforcement
  • Glass fiber reinforced material, 30% filler by weight
Additive
  • PTFE lubricant (10%)
  • Silicone lubricant
Features
  • Lubrication
RoHS Compliance
  • Contact manufacturer
Appearance
  • Black
  • Natural color
Forms
  • Particle
Processing Method
  • Injection molding
PhysicalNominal ValueUnitTest Method
Specific Gravity 1.44g/cm³ASTM D792
Molding Shrinkage - Flow (3.18 mm)0.40%ASTM D955
Water Absorption (23°C, 24 hr)0.60%ASTM D570
MechanicalNominal ValueUnitTest Method
Tensile Modulus 10300MPaASTM D638
Tensile Strength 165MPaASTM D638
Tensile Elongation (Break)2.0%ASTM D638
Flexural Modulus 8960MPaASTM D790
Flexural Strength 241MPaASTM D790
Coefficient of Friction ASTM D1894
    With Metal-Dynamic 0.24ASTM D1894
    With metal-static 0.23ASTM D1894
ImpactNominal ValueUnitTest Method
Notched Izod Impact (3.18 mm)96J/mASTM D256
Unnotched Izod Impact (3.18 mm)960J/mASTM D4812
ThermalNominal ValueUnitTest Method
Deflection Temperature Under Load ASTM D648
    0.45 MPa, not annealed 241°CASTM D648
    1.8 MPa, not annealed 235°CASTM D648
ElectricalNominal ValueUnitTest Method
Volume Resistivity 1.0E+14ohms·cmASTM D257
FlammabilityNominal ValueUnitTest Method
Flame Rating (1.59 mm)HBUL 94
Additional Information
Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 6mil/in.Tensile Elongation, ASTM D-638: 2-3%Wear Factor, K, ASTM D-3702: 25E-10in³/min/ft/lb/hrCoefficient of Friction, Dynamic, ASTM D-3702: 0.24Coefficient of Friction, Static, ASTM D-3702: 0.23The wear factor and dynamic coefficient of friction were both tested on a Falex Model No.6 Wear Testing Machine at 50 FPM, 2000 PV, against C1018 steel of hardness 15-25 Rockwell C, 14-17 micro smoothness.
InjectionNominal ValueUnit
Drying Temperature 79.4°C
Drying Time 4.0hr
Suggested Max Moisture 0.20%
Suggested Max Regrind 20%
Rear Temperature 274 - 288°C
Middle Temperature 274 - 288°C
Front Temperature 274 - 288°C
Mold Temperature 65.6 - 93.3°C
Injection Pressure 82.7 - 138MPa
Resin Grade Manufacturer Category Trademark
Miramid® VE50C BASF Leuna GmbH Nylon 6 Miramid®
Mirakutoran® TPU E559 Japan Mirakutoran Inc. TPU Alloy Mirakutoran® TPU
Sindustris PC GN5202F Sincerity Australia Pty Ltd. PC+ABS Sindustris PC
Sylvin 6238-75 Yellow 4196 Sylvin Technologies Incorporated PVC, Unspecified Sylvin
Sumiliteresin® PR-2400 I SBHPP Phenolic Sumiliteresin®