ACCUTECH™ HP0336G20C002L
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 5eHiBm_ACCUTECH-HP0336G20C002L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ACCUTECH™HP0336G20C002L is a polypropylene homopolymer (PP Homopoly) product, and its filler is 20% glass fiber reinforced material. It is available in North America. Typical application areas are: water pipes/pipes/drinking water. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| UL File Number |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2900 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 52.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 4.0 | % | ASTM D638 |
| Fracture | 6.0 | % | ASTM D638 |
| Flexural Modulus | 3700 | MPa | ASTM D790 |
| Flexural Strength | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 152 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 20% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® MPG | Röchling Engineering Plastics SE & Co. KG | UHMWPE | POLYSTONE® |
| Vi-Chem PVC VNC87-40E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| TOYOBO Urethane E3070A | TOYOBO America, Inc. | PUR-Ether | TOYOBO Urethane |
| Cevian®-V CGR30F | Daicel Polymer Ltd. | ABS | Cevian®-V |
| FRblend® PP-1305 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP, Unspecified | FRblend® |